A mixed matrix membrane is provided which comprises a continuous phase organic polymer and small pore molecular sieves dispersed therein. The molecular sieves have a largest minor crystallographic free diameter of 3.6 Angstroms or less. When these molecular sieves are properly interspersed with a continuous phase polymer, the membrane will exhibit a mixed matrix membrane effect, i.e., a selectivity increase of at least 10% relative to a neat membrane containing no molecular sieves. Finally, methods for making and using such mixed matrix membranes to separate gases from a mixture containing two or more gases are also disclosed.
A mixed matrix membrane is provided which comprises a continuous phase organic polymer and small pore alumina containing molecular sieves dispersed therein. The molecular sieves have a silica-to-alumina molar ratio of less than 1.0, more preferably, less than 0.3, and most preferably less than 0.1. In some cases, the molecular sieves have no appreciable amounts of silica. Exemplary compositions include aluminophosphates (AlPO) and silicoaluminophosphates (SAPO). When these molecular sieves are properly interspersed with a continuous phase polymer, the membrane will exhibit a mixed matrix membrane effect, i.e., a selectivity increase of at least 10% relative to a neat membrane containing no molecular sieves. The molecular sieves have pores with a largest minor crystallographic free diameter of 4.0 Angstroms or less. Finally, methods for making and using such mixed matrix membranes to separate gases from a mixture containing two or more gases are also disclosed.
A mixed matrix membrane is provided which comprises a continuous phase organic polymer and small pore alumina containing molecular sieves dispersed therein. The molecular sieves have a silica-to-alumina molar ratio of less than 1.0, more preferably, less than 0.3, and most preferably less than 0.1. In some cases, the molecular sieves have no appreciable amounts of silica. Exemplary compositions include aluminophosphates (AIPO) and silicoaluminophosphates (SAPO). When these molecular sieves are properly interspersed with a continuous phase polymer, the membrane will exhibit a mixed matrix membrane effect, i.e., a selectivity increase of at least 10% relative to a neat membrane containing no molecular sieves. The molecular sieves have pores with a largest minor crystallographic free diameter of 4.0 Angstroms or less. The molecular sieves may be selected from the group having IZA structure types including AEI, CHA, ERI, LEV, AFX, AFT, and GIS. Examples of preferred molecular sieves include: AIPO-18, SAPO-18, AIPO-34, SAPO-34, SAPO-44, SAPO-47, AIPO-17, SAPO-17, CVX-7, SAPO-35, SAPO-56, ALPO-52, and SAPO-43. Finally, methods for making and using such mixed matrix membranes to separate gases from a mixture containing two or more gases are also disclosed.
A mixed matrix membrane is provided which comprises a continuous phase organic polymer and small pore molecular sieves dispersed therein. The molecular sieves have a largest minor crystallographic free diameter of 3.6 Angstroms or less. When these molecular sieves are properly interspersed with a continuous phase polymer, the membrane will exhibit a mixed matrix membrane effect, i.e., a selectivity increase of at least 10% relative to a neat membrane containing no molecular sieves. Finally, methods for making and using such mixed matrix membranes to separate gases from a mixture containing two or more gases are also disclosed.
A composition of and a method of making high performance mixed matrix hollow fiber membranes is described. The membranes have a high resistance to plasticization by use of a predetermined amount of crosslinking. The preferred polymer material for the membrane is a polyimide polymer continuous phase comprising ester crosslinks and a molecular sieve material dispersed within the polymer continuous phase. The resultant mixed matrix hollow fiber membrane exhibits a high permeance of CO.sub.2 in combination with a high CO.sub.2 /CH.sub.4 selectivity. Another embodiment provides a method of making the mixed matrix hollow fiber membrane from a monesterified polymer followed by final crosslinking after hollow fiber formation.